Soluble fluorinated polyimides that contain curable acetylene units in the backbone
Conference
·
OSTI ID:141588
- Toyohashi Univ. of Technology, Aichi (Japan)
Soluble polyimides that contain internal acetylene groups in the backbone were prepared by reacting 2,2-bis(3,4-dicarboxyphenyl)hexafluoropropane dianhydride with various ratio of bis(3-aminophenyl)acetylene and 4,4`-diaminodiphenyl ether. The polyimides were soluble in organic solvents such as N-methylpyrrolidone (NMP) and N,N-dimethylacetamide, and exhibited reduced viscosities in the range of 0.76-1.44 (in NMP at 30{degrees}C). The crosslinking behavior was examined by DSC. The onset of exotherm appeared at 321-345{degrees}C depending on the acetylene content. After thermal treatment at 350{degrees}C, the polyimides became insoluble in any organic solvents examined and in conc. sulfuric acid. The viscoelastic analyses showed the effect of crosslinking clearly. For example, Tg increased with thermal treatment, and was finally above 400{degrees}C. The drop of modulus at higher temperature also became very small. The TGA analyses also showed excellent thermal stability.
- OSTI ID:
- 141588
- Report Number(s):
- CONF-930304--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Internal acetylene unit as a cross-link site for polyimides
Enhancement of dimensional stability in soluble polyimides via lanthanide(III) acetate additives
Low dielectric constant fibers from a fluorinated polymide for electronic packaging
Conference
·
Thu Nov 30 23:00:00 EST 1995
·
OSTI ID:126967
Enhancement of dimensional stability in soluble polyimides via lanthanide(III) acetate additives
Journal Article
·
Sun Mar 31 23:00:00 EST 1996
· Journal of Advanced Materials
·
OSTI ID:263169
Low dielectric constant fibers from a fluorinated polymide for electronic packaging
Conference
·
Tue Oct 01 00:00:00 EDT 1996
·
OSTI ID:370890