Flame retardant brominated styrene-based polymers. I. Synthesis, characterization and application of dibromostyrene and butadiene copolymers
Conference
·
OSTI ID:141557
- Great Lakes Chemical Corporation, West Lafayette, IN (United States)
Brominated styrene-based polymers having surprisingly good physical properties in combination with flame retardancy are prepared from copolymers of dibromostyrene and butadiene. Polymerization compositions were measured by bromine contents (% Br) of the polymers by Schoeninger Combustion Method. Weight losses (% loss) were measured at 20{degrees}C/min by Thermogravimetric Analysis (TGA). Molecular weights were measured by GPC based on a standard molecular weight (MW) of polystyrene (PS). Flammability of the latex products when used in textile backcoatings was tested by Motor Vehicle Safety Standard 302 (MVSS-302) flammability test.
- OSTI ID:
- 141557
- Report Number(s):
- CONF-930304--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Flame retardant brominated styrene-based polymers. II. Synthesis, characterization and application of dibromostyrene, styrene and butadiene terpolymers
Flame retardant brominated styrene-based polymers. VII. Applications of dibromostyrene graft latices
Flame retardant brominated styrene-based polymers. VI. Synthesis and characterization of dibromostyrene graft latices
Conference
·
Thu Dec 30 23:00:00 EST 1993
·
OSTI ID:141558
Flame retardant brominated styrene-based polymers. VII. Applications of dibromostyrene graft latices
Conference
·
Thu Nov 30 23:00:00 EST 1995
·
OSTI ID:126875
Flame retardant brominated styrene-based polymers. VI. Synthesis and characterization of dibromostyrene graft latices
Conference
·
Thu Nov 30 23:00:00 EST 1995
·
OSTI ID:126874