Three-Dimensional Microstructural Imaging of Sulfur Poisoning-Induced Degradation in a Ni-YSZ Anode of Solid Oxide Fuel Cells
- Research Organization:
- Energy Frontier Research Centers (EFRC) (United States). Heterogeneous Functional Materials Center (HeteroFoaM)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- SC0001061
- OSTI ID:
- 1383947
- Journal Information:
- Scientific Reports, Vol. 4, Issue 1; Related Information: HeteroFoaM partners with University of South Carolina (lead); University of California, Santa Barbara; University of Connecticut; Georgia Institute of Technology; Princeton University; Rochester Institute of Technology; Savannah River National Laboratory; University of South Carolina; University of Utah; ISSN 2045-2322
- Publisher:
- Nature Publishing Group
- Country of Publication:
- United States
- Language:
- English
Similar Records
Three-Dimensional Microstructural Imaging of Hydrogen Sulfide Poisoning-induced Degradation in Ni-YSZ Solid Oxide Fuel Cells
Three-dimensional microstructural changes in the Ni-YSZ solid oxide fuel cell anode during operation
Three-dimensional microstructural changes in the Ni–YSZ solid oxide fuel cell anode during operation
Journal Article
·
Tue Jun 10 00:00:00 EDT 2014
· Scientific Reports
·
OSTI ID:1383947
+6 more
Three-dimensional microstructural changes in the Ni-YSZ solid oxide fuel cell anode during operation
Journal Article
·
· Acta Materialia
·
OSTI ID:1383947
+9 more
Three-dimensional microstructural changes in the Ni–YSZ solid oxide fuel cell anode during operation
Journal Article
·
Tue May 01 00:00:00 EDT 2012
· Acta Materialia
·
OSTI ID:1383947
+9 more