Combined DFT and Microkinetic Modeling Study of Hydrogen Oxidation at the Ni/YSZ Anode of Solid Oxide Fuel Cells
Journal Article
·
· Journal of Physical Chemistry Letters
- Department of Chemical Engineering, University of South Carolina, 301 South Main Street, Columbia, South Carolina 29208, United States
- Research Organization:
- Energy Frontier Research Centers (EFRC) (United States). Heterogeneous Functional Materials Center (HeteroFoaM)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- DOE Contract Number:
- SC0001061
- OSTI ID:
- 1383065
- Journal Information:
- Journal of Physical Chemistry Letters, Vol. 3, Issue 19; Related Information: HeteroFoaM partners with University of South Carolina (lead); University of California, Santa Barbara; University of Connecticut; Georgia Institute of Technology; Princeton University; Rochester Institute of Technology; Savannah River National Laboratory; University of South Carolina; University of Utah; ISSN 1948-7185
- Publisher:
- American Chemical Society
- Country of Publication:
- United States
- Language:
- English
Similar Records
Three-dimensional microstructural changes in the Ni-YSZ solid oxide fuel cell anode during operation
Three-dimensional microstructural changes in the Ni–YSZ solid oxide fuel cell anode during operation
Three-Dimensional Microstructural Imaging of Sulfur Poisoning-Induced Degradation in a Ni-YSZ Anode of Solid Oxide Fuel Cells
Journal Article
·
· Acta Materialia
·
OSTI ID:1383065
+9 more
Three-dimensional microstructural changes in the Ni–YSZ solid oxide fuel cell anode during operation
Journal Article
·
Tue May 01 00:00:00 EDT 2012
· Acta Materialia
·
OSTI ID:1383065
+9 more
Three-Dimensional Microstructural Imaging of Sulfur Poisoning-Induced Degradation in a Ni-YSZ Anode of Solid Oxide Fuel Cells
Journal Article
·
Tue Jun 10 00:00:00 EDT 2014
· Scientific Reports
·
OSTI ID:1383065
+6 more