Synthesis of Pt3Y and Other Early–Late Intermetallic Nanoparticles by Way of a Molten Reducing Agent
- Univ. of California, Berkeley, CA (United States)
- BASF SE (Germany)
- hte GmbH - a subsidiary of BASF, Heidelberg (Germany)
- BASF SE (Germany); Univ. of California, Berkeley, CA (United States)
- Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
- Univ. of California, Berkeley, CA (United States); Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States); Kavli Energy NanoScience Institute, Berkeley, CA (United States)
Early–late intermetallic phases have garnered increased attention recently for their catalytic properties. To achieve the high surface areas needed for industrially relevant applications, these phases must be synthesized as nanoparticles in a scalable fashion. Herein, Pt3Y—targeted as a prototypical example of an early–late intermetallic—has been synthesized as nanoparticles approximately 5–20 nm in diameter via a solution process and characterized by XRD, TEM, EDS, and XPS. The key development is the use of a molten borohydride (MEt3BH, M = Na, K) as both the reducing agent and reaction medium. Readily available halide precursors of the two metals are used. Accordingly, no organic ligands are necessary, as the resulting halide salt byproduct prevents sintering, which further permits dispersion of the nanoscale intermetallic onto a support. The versatility of this approach was validated by the synthesis of other intermetallic phases such as Pt3Sc, Pt3Lu, Pt2Na, and Au2Y.
- Research Organization:
- Lawrence Berkeley National Laboratory (LBNL), Berkeley, CA (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC), Basic Energy Sciences (BES)
- Grant/Contract Number:
- AC02-05CH11231
- OSTI ID:
- 1379819
- Journal Information:
- Journal of the American Chemical Society, Vol. 139, Issue 16; ISSN 0002-7863
- Publisher:
- American Chemical Society (ACS)Copyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Similar Records
From the Nonexistent Polar Intermetallic Pt3Pr4 via Pt2–xPr3 to Pt/Sn/Pr Ternaries
Identification of a Pt3Co Surface Intermetallic Alloy in Pt–Co Propane Dehydrogenation Catalysts