Residual strength of a thermomechanically fatigued TIMETAL 21S/SCS-6 composite
Journal Article
·
· Journal of Materials Engineering and Performance
- SRI International, Menlo Park, CA (United States)
The factors contributing to the residual strength of a thermomechanically-fatigued SiC fiber-reinforced metal matrix composite were assessed based on fracture surface features. The estimated residual strength was found to be in reasonable agreement with the measured value.
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 136971
- Journal Information:
- Journal of Materials Engineering and Performance, Vol. 4, Issue 5; Other Information: PBD: Oct 1995
- Country of Publication:
- United States
- Language:
- English
Similar Records
Characterization of damage progression in SCS-6/Timetal 21S (0)4 under thermomechanical fatigue loadings
Characterization of damage progression in SCS-6/TIMETAL 21S [0]{sub 4} under thermomechanical fatigue loading
Thermomechanical fatigue damage/failure mechanisms in SCS-6/Timetal 21S (0/90)s composite. Final report
Conference
·
Tue Nov 01 00:00:00 EST 1994
·
OSTI ID:136971
Characterization of damage progression in SCS-6/TIMETAL 21S [0]{sub 4} under thermomechanical fatigue loading
Conference
·
Tue Dec 31 00:00:00 EST 1996
·
OSTI ID:136971
Thermomechanical fatigue damage/failure mechanisms in SCS-6/Timetal 21S (0/90)s composite. Final report
Technical Report
·
Wed Jun 01 00:00:00 EDT 1994
·
OSTI ID:136971