Report detailing comparative analysis of results from high flux isotope reactor and national institute of standards technology small-angle neutron scattering experiments

Technical Report · Tue Sep 01 04:00:00 EDT 2015

DOI:https://doi.org/10.2172/1364278· OSTI ID:1364278

Sokolov, Mikhail A. ^[1]; Littrell, Ken ^[1]; Wells, Peter ^[2]; Cunningham, Nicholas J. ^[2]

---

1. Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)
2. Univ. of California, Santa Barbara, CA (United States)

The major issues regarding irradiation effects are discussed in [1-3] and have also been discussed in previous progress and milestone reports. As noted previously, of the many significant issues discussed, the issue considered to have the most impact on the current regulatory process is that associated with effects of neutron irradiation on RPV steels at high fluence, for long irradiation times, and as affected by neutron flux. It is clear that embrittlement of RPV steels is a critical issue that may limit LWR plant life extension. The primary objective of the LWRSP RPV task is to develop robust predictions of transition temperature shifts (TTS) at high fluence ( t) to at least 1020 n/cm² (>1 MeV) pertinent to plant operation of some pressurized water reactors (PWR) for 80 full power years. Correlations between the high flux test reactor results and low flux surveillance specimens must be established for proper RPV embrittlement predictions of the current nuclear power fleet. Additionally, a complete understanding of defect evolution for high nickel RPV steels is needed to characterize the embrittlement potential of Mn-Ni-enriched precipitates (MNPs), particularly for the high fluence regime. While understanding of copper-enriched precipitates (CRPs) have been fully developed, the recent discovery and experimental verification [4] of late blooming MNPs with little to no copper for nucleation has stimulated research efforts to understand the evolution of these phases. New and existing databases will be combined to support developing physically based models of TTS for high fluence-low flux ( < 10 11n/cm²-s) conditions, beyond the existing surveillance database, to neutron fluences of at least 1 1020 n/cm2 (>1 MeV). Moreover, large number of various RPV materials have been irradiated in ATR-2 experiment and will be jointly studied by University of California Santa Barbara (UCSB) and ORNL to address majority of microstructural characteristics discussed above, see Ref. [5] and [6] for details. UCSB has performed a large number of SANS experiments in the past at the National Institute of Standards and Technology (NIST) Center for Neutron Research (NCNR). These data are taken from RPV steels irradiated in a wide range of flux-fluence space and will be very useful in comparing to the upcoming UCSB ATR-2 irradiation characterization since most of the SANS experiments with ATR-2 materials will be performed at ORNL High Flux Isotope Reactor (HFIR). However in the previous report [7], some discrepancies were observed between HFIR and NCNR generated data. One of the hypotheses was that there was some kind of extra scattering occurring off the sample holders that results in the HFIR curves falling above the NCNR curves. To test this hypothesis, UCSB provided thermally aged samples that have been previously run at NCNR to ORNL for testing at HFIR while ORNL performed some improvements to experimental set up at HFIR. This report provides the status for the Level 3 Milestone (M3LW-15OR0402013), Complete report detailing comparative analysis of results from High Flux Isotope Reactor and National Institute of Standards and Technology small-angle neutron scattering experiments. This milestone is associated with small-angle neutron scattering characterization at the High Flux Isotope Reactor of various model alloys that had been previously characterized at NCNR by UCSB.

• Research Organization: Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States). High Flux Isotope Reactor (HFIR)
• Sponsoring Organization: USDOE
• DOE Contract Number: AC05-00OR22725
• OSTI ID: 1364278
• Report Number(s): ORNL/LTR--2015/423; RC0304000; NERC006
• Country of Publication: United States
• Language: English

Related Subjects

21 SPECIFIC NUCLEAR REACTORS AND ASSOCIATED PLANTS