Precursor evolution and SCC initiation of cold-worked alloy 690 in simulated PWR primary water
Stress corrosion crack initiation of two thermally-treated, cold-worked (CW) alloy 690 materials was investigated in 360oC simulated PWR primary water using constant load tensile (CLT) tests and blunt notch compact tension (BNCT) tests equipped with direct current potential drop (DCPD) for in-situ detection of cracking. SCC initiation was not detected by DCPD for the 21% and 31%CW CLT specimens loaded at their yield stress after ~9,220 h, however intergranular (IG) precursor damage and isolated surface cracks were observed on the specimens. The two 31%CW BNCT specimens loaded at moderate stress intensity after several cyclic loading ramps showed DCPD-indicated crack initiation after 10,400h exposure at constant stress intensity, which resulted from significant growth of IG cracks. The 21%CW BNCT specimens only exhibited isolated small IG surface cracks and showed no apparent DCPD change throughout the test. Interestingly, post-test cross-section examinations revealed many grain boundary (GB) nano-cavities in the bulk of all the CLT and BNCT specimens particularly for the 31%CW materials. Cavities were also found along GBs extending to the surface suggesting an important role in crack nucleation. This paper provides an overview of the evolution of GB cavities and will discuss their effects on crack initiation in CW alloy 690.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US), Environmental Molecular Sciences Laboratory (EMSL)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1358515
- Report Number(s):
- PNNL-SA-121146; 49159; 830403000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Precursor Evolution and Stress Corrosion Cracking Initiation of Cold-Worked Alloy 690 in Simulated Pressurized Water Reactor Primary Water
Characterization of SCC Initiation Precursors in Cold-Worked Alloy 690
Crack Initiation Behavior of Cold-Worked Alloy 690 in Simulated PWR Primary Water - Role of Starting Microstructure, Applied Stress and Cold Work on Precursor Damage Evolution
Journal Article
·
Mon May 22 00:00:00 EDT 2017
· Corrosion
·
OSTI ID:1378041
Characterization of SCC Initiation Precursors in Cold-Worked Alloy 690
Conference
·
Mon Mar 27 00:00:00 EDT 2017
·
OSTI ID:1358511
Crack Initiation Behavior of Cold-Worked Alloy 690 in Simulated PWR Primary Water - Role of Starting Microstructure, Applied Stress and Cold Work on Precursor Damage Evolution
Conference
·
Mon Sep 30 00:00:00 EDT 2019
·
OSTI ID:1605409