New insights on electro-optical response of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) film to humidity
- ORNL
Understanding the relative humidity (RH) response of poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) is critical for improving the stability of organic electronic devices and developing selective sensors. In this work combined gravimetric sensing, nanoscale surface probing, and mesoscale optoelectronic characterization are used to directly compare the RH dependence of electrical and optical conductivities and unfold connections between the rate of water adsorption and changes in functional properties of PEDOT:PSS film. We report three distinct regimes where changes in electrical conductivity, optical conductivity, and optical bandgap are correlated with the mass of adsorbed water. At low (RH < 25%) and high (RH > 60%) humidity levels dramatic changes in electrical, optical and structural properties occur, while changes are insignificant in mid-RH (25% < RH < 60%) conditions. We associate the three regimes with water adsorption at hydrophilic moieties at low RH, diffusion and swelling throughout the film at mid-RH, and saturation of the film by water at high RH. Optical film thickness increased by 150% as RH was increased from 9% to 80%. Low frequency (1 kHz) impedance increased by ~100% and film capacitance increased by ~30% as RH increased from 9% to 80% due to an increase in the film dielectric constant. Finally, changes in electrical and optical conductivities concomitantly decrease across the full range of RH tested.
- Research Organization:
- Oak Ridge National Laboratory (ORNL), Oak Ridge, TN (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- Grant/Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1357981
- Journal Information:
- ACS Applied Materials and Interfaces, Vol. 9, Issue 18; ISSN 1944-8244
- Publisher:
- American Chemical Society (ACS)Copyright Statement
- Country of Publication:
- United States
- Language:
- English
Web of Science
Similar Records
Electron-phonon coupling modification and carrier mobility enhancement in poly(3,4-ethylenedioxythiophene) doped with poly(4-styrenesulfonate) films by ultraviolet irradiation
Increasing the work function of poly(3,4-ethylenedioxythiophene) doped with poly(4-styrenesulfonate) by ultraviolet irradiation