Development of Metallic Fuels for Actinide Transmutation
- Idaho National Laboratory
Research and development activities on metallic fuels are focused on their potential use for actinide transmutation in future sodium fast reactors. As part of this application, there is also a need for a near zero-loss fabrication process and a desire to demonstrate a multifold increase in burnup potential. The incorporation of Am and Np into the traditional U-20Pu-10Zr metallic fuel alloy was demonstrated in the US during the Integral Fast Reactor Program of the 1980’s and early 1990’s. However, the conventional counter gravity injection casting method performed under vacuum, previously used to fabricate these metallic fuel alloys, was not optimized for mitigating loss of the volatile Am constituent in the casting charge; as a result, approximately 40% of the Am casting charge failed to be incorporated into the as-cast fuel alloys. Fabrication development efforts of the past few years have pursued an optimized bottom-pour casting method to increase utilization of the melted charge to near 100%, and a differential pressure casting approach, performed under an argon overpressure, has been demonstrated to result in essentially no loss of Am due to volatilization during fabrication. In short, a path toward zero-loss fabrication of metallic fuels including minor actinides has been shown to be feasible. Irradiation testing of advanced metallic fuel alloys in the Advanced Test Reactor (ATR) has been underway since 2003. Testing in the ATR is performed inside of cadmium-shrouded positions to remove >99% of the thermal flux incident on the test fuels, resulting in an epi-thermal driven fuel test that is free from gross flux depression and producing an essentially prototypic radial temperature profile inside the fuel rodlets. To date, three irradiation test series (AFC-1,2,3) have been completed. Over 20 different metallic fuel alloys have been tested to burnups as high as 30% with constituent compositions of Pu up to 30%, Am up to 12%, Np up to 10%, and Zr between 10 and 60%. In general, the performance of all of these substantially disparate metallic fuel alloys has been observed to be excellent, and their irradiation behaviors are generally consistent with historic norms for metallic fuels without minor actinide additions and having lower Pu or Zr contents. Future work is being undertaken with a view toward increasing the burnup potential of metallic fuels even more. Design innovations under investigation include: 1) lowering the fuel smear density in order to accommodate more swelling, 2) annular fuel geometry to eliminate the need for a sodium bond, 3) minor alloy additions to stabilize lanthanide fission products inside the fuel and prevent their transport to the cladding where they can participate in fuel-cladding chemical interaction (FCCI), and 4) coatings/liners on the cladding inner surface to mitigate FCCI and enable higher temperature operation. This paper will present the current state of development of metallic fuels for actinide transmutation in the US. Highlights will include recent results from metallic fuel casting experiments, experiments to identify alloy additions to immobilize lanthanide fission products, and postirradiation examinations of annular metallic fuels at low burnup.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- AC07-05ID14517
- OSTI ID:
- 1356071
- Report Number(s):
- INL/CON-14-33967
- Resource Relation:
- Conference: GLOBAL 2015, Paris, France, 9/20/2015 - 9/24/2015
- Country of Publication:
- United States
- Language:
- English
Similar Records
Transmutation Fuels Development in the Advanced Fuels Campaign
Microstructural Characteristics of U-Zr Ingot Slug and Atomized Powder for SFR metal Fuel