Effect of Nb2O5 and V2O5 addition on the superconducting properties of YBa2Cu3O(y) thin films
- Tata Inst. of Fundamental Research, Bombay (India)
The effect of Nb2O5 and V2O5 addition on the superconducting properties and microstructure of YBa2Cu3O(y) has been studied in thin films. Polycrystalline targets for laser ablation were prepared by mixing high purity V2O5 or Nb2O5 powders with a well characterized YBa2Cu3O(y) powder in the range 0 to 4 wt percent by solid state reaction method. Thin films (approximately 1500 A thickness) of the above targets were grown on (100) SrTiO3 (STO) and (100) LaAlO3 (LAO) substrates at 700 C temperature by pulsed laser deposition (PLD) technique. In the case of Nb2O5 addition the authors have noticed an increase in J(sub c) up to 0.5 wt percent and higher additive concentration (greater than 0.5 wt percent) have degraded the superconducting properties. However, in the case of V2O3 addition, there is an improvement in current density and microstructural properties up to 1 wt percent and the superconducting properties degrade for concentrations greater than 1 wt percent. The best J{sub c} for 0.5 wt percent of Nb2O5 added to YBCO thin film is 1.6 x 10(exp 6) A/sq cm and for that of V2O5 added sample is 3.4 x 10(exp 6) A/sq cm at 77 K as compared to the pure YBa2Cu3O(y) (YBCO) film J{sub c} (1.2 x 10(exp 6) A/sq cm) observed on STO substrates. The reason for improvement in J{sub c} and microstructural properties in the case of V2O5 addition could be due to the low melting of V2O5 (690 C) which can act as a very good surfactant during deposition. Over all, the authors have realized that Nb2O5 addition or V2O5 addition to YBCO have shown significant improvement over the undoped YBa2Cu3O(7-x) films grown under identical conditions.
- Research Organization:
- National Aeronautics and Space Administration, Houston, TX (United States). Lyndon B. Johnson Space Center
- OSTI ID:
- 135359
- Report Number(s):
- N--96-10230; NASA-CP--3290-VOL-1; S--792-VOL-1; NAS--1.55:3290-VOL-1; CONF-940627--
- Country of Publication:
- United States
- Language:
- English
Similar Records
Growth and micro structural studies on Yittria Stabilized Zirconia (YSZ) and Strontium Titanate (STO) buffer layers
Superconductivity devices: Commercial use of space. Annual Report, 3 Jul. 1991 - 2 Jul. 1992