Characterization of BOR-60 Irradiated 14YWT-NFA1 Tubes
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
Tubes of FCRD 14YWT-NFA1 Alloy were placed in the BOR-60 reactor and irradiated under a fast flux neutron environment to two conditions: 7 dpa at 360-370 °C and 6 dpa at 385-430 °C. Small sections of the tube were cut and sent to UC Berkeley for nanohardness testing and focused ion beam (FIB) milling of TEM specimens. FIB specimens were sent back to LANL for final FIB milling and TEM imaging. Hardness data and TEM images are presented in this report. This is the first fast reactor neutron irradiated information on the 14YWT-NFA1 alloy.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- AC52-06NA25396
- OSTI ID:
- 1344339
- Report Number(s):
- LA--UR-17-21204
- Country of Publication:
- United States
- Language:
- English
Similar Records
Post Irradiation Examination of Fast Neutron Irradiated 14YWT Tubes at Nuclear Science User Facilities
Shear Punch Testing of BOR-60 Irradiated TEM Specimens
Void Swelling and Microstructure of Austenitic Stainless Steels Irradiated in the BOR - 60 Reactor
Journal Article
·
Sat Jul 01 00:00:00 EDT 2017
· Transactions of the American Nuclear Society
·
OSTI ID:23047436
Shear Punch Testing of BOR-60 Irradiated TEM Specimens
Technical Report
·
Tue Jun 13 00:00:00 EDT 2017
·
OSTI ID:1363742
Void Swelling and Microstructure of Austenitic Stainless Steels Irradiated in the BOR - 60 Reactor
Technical Report
·
Thu Nov 01 00:00:00 EDT 2012
·
OSTI ID:1224950