Liquid-phase diffusion bonding: Temperature effects and solute redistribution in high temperature lead-free composite solders
Conference
·
OSTI ID:1337658
- Ames Lab. and Iowa State Univ., Ames, IA (United States); Iowa State Univ., Ames, IA (United States)
Liquid-phase diffusion bonding (LPDB) is being studied as the primary phenomena occurring in the development of a high temperature lead-free composite solder paste composed of gas-atomized Cu-10Ni, wt.% (Cu-11Ni, at.%) powder blended with Sn-0.7Cu-0.05Ni-0.01Ge (Sn-1.3Cu-0.1Ni-0.02Ge, at.%) Nihon-Superior SN100C solder powder. Powder compacts were used as a model system. LPDB promotes enhanced interdiffusion of the low-melting alloy matrix with the solid Cu-10Ni reinforcement powder above the matrix liquidus temperature. The initial study involved the effective intermetallic compound (IMC) compositions and microstructures that occur at varying reflow temperatures and times between 250-300°C and 30-60s, respectively. Certain reflow temperatures encourage adequate interdiffusion to form a continuous highly-conductive network throughout the composite solder joints. The diffusion of nickel, in particular, has a disperse pattern that foreshadows the possibility of a highly-conductive low-melting solder that can be successfully utilized at high temperatures.
- Research Organization:
- Ames Lab., Ames, IA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC02-07CH11358
- OSTI ID:
- 1337658
- Report Number(s):
- IS--M 970
- Country of Publication:
- United States
- Language:
- English
Similar Records
Stability of molybdenum nanoparticles in Sn-3.8Ag-0.7Cu solder during multiple reflow and their influence on interfacial intermetallic compounds
Effect of Ag3Sn nanoparticles and temperature on Cu6Sn5 IMC growth in Sn-xAg/Cu solder joints
Rapid Solidification of Sn-Cu-Al Alloys for High-Reliability, Lead-Free Solder: Part II. Intermetallic Coarsening Behavior of Rapidly Solidified Solders After Multiple Reflows
Journal Article
·
Tue Feb 14 23:00:00 EST 2012
· Materials Characterization
·
OSTI ID:22066416
Effect of Ag3Sn nanoparticles and temperature on Cu6Sn5 IMC growth in Sn-xAg/Cu solder joints
Journal Article
·
Thu Mar 15 00:00:00 EDT 2018
· Materials Research Bulletin
·
OSTI ID:22805453
Rapid Solidification of Sn-Cu-Al Alloys for High-Reliability, Lead-Free Solder: Part II. Intermetallic Coarsening Behavior of Rapidly Solidified Solders After Multiple Reflows
Journal Article
·
Wed Oct 05 20:00:00 EDT 2016
· Metallurgical and Materials Transactions. A, Physical Metallurgy and Materials Science
·
OSTI ID:1417370