Improved Wetting Characteristics in TiO2–Modified Ag-CuO Air Braze Filler Metals
A silver-based joining technique referred to as reactive air brazing (RAB) has been recently developed for joining high temperature structural ceramic components of the type used in high-temperature electrochemical devices. In prior work, it was found that additions of CuO to silver have a significant effect on the wettability and joint strength characteristics of the resulting braze on polycrystalline alumina substrates. More recently, it has been found that by adding as little as 0.5 mol % titania to these Ag-CuO brazes, the wettability of the RAB on alumina surfaces is further enhanced. The results of wettabilty measurements of Ag-CuO-TiO2 RAB compositions on alumina will be presented along with the microstructural characterization of Ag-CuO-TiO2 braze joints in alumina.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1240239
- Report Number(s):
- PNNL-SA-47943; AA6010000
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effects of CuO Content on the Wetting Behavior and Mechanical Properties of a Ag-CuO Braze for Ceramic Joining
TiO2-modified Ag-CuO Reactive Air Brazes for Improved Wettability on Mixed Ionic/Electronic Conductors