Electromagnetic Properties of (Gd, Y)Ba2Cu3Ox Superconducting Tapes With High Levels of Zr Addition
Journal Article
·
· IEEE Transactions on Applied Superconductivity
The dependence of the critical current density (J(c)) on the orientation of applied magnetic fields was studied in Zr-doped (Gd, Y)Ba2Cu3Ox tapes fabricated by metal organic chemical vapor deposition. The in-field performance of J(c) of (Gd, Y)Ba2Cu3Ox tapes with Zr-doping levels of 7.5-30 at.% was investigated up to 5 T over a temperature range of 40-77 K. The highest critical currents (I-c) at H parallel to c and the highest values of minimum Ic in angular dependence measurements were achieved in the tapes with 20% Zr doping over a broad range of temperature and magnetic field conditions measured. The electromagnetic properties have been related to the changes in BaZrO3 content and microstructure.
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- DOE Contract Number:
- DE-AR0000196
- OSTI ID:
- 1211408
- Journal Information:
- IEEE Transactions on Applied Superconductivity, Vol. 23, Issue 3; ISSN 1051-8223
- Country of Publication:
- United States
- Language:
- English
Similar Records
High critical currents in heavily doped (Gd,Y)Ba2Cu3Ox superconductor tapes
Enhanced critical currents in (Gd,Y)Ba2Cu3Ox superconducting tapes with high levels of Zr addition
The Structural Evolution of (Gd, Y)Ba2Cu3Ox Tapes With Zr Addition Made by Metal Organic Chemical Vapor Deposition
Journal Article
·
Mon Jan 19 00:00:00 EST 2015
· Applied Physics Letters
·
OSTI ID:1211408
+3 more
Enhanced critical currents in (Gd,Y)Ba2Cu3Ox superconducting tapes with high levels of Zr addition
Journal Article
·
Mon Jan 21 00:00:00 EST 2013
· Superconductor Science and Technology
·
OSTI ID:1211408
+9 more
The Structural Evolution of (Gd, Y)Ba2Cu3Ox Tapes With Zr Addition Made by Metal Organic Chemical Vapor Deposition
Journal Article
·
Sat Jun 01 00:00:00 EDT 2013
· IEEE Transactions on Applied Superconductivity
·
OSTI ID:1211408
+7 more