Textured Nd2Fe14B flakes with enhanced coercivity

Journal Article · Sun Apr 01 00:00:00 EDT 2012 · Journal of Applied Physics

DOI:https://doi.org/10.1063/1.3679425· OSTI ID:1211306

Cui, BZ; Zheng, LY; Marinescu, M; Liu, JF; Hadjipanayis, GC

Morphology, structure, and magnetic properties of the [001] textured Nd2Fe14B nanocrystalline flakes prepared by surfactant-assisted high energy ball milling (HEBM) and subsequent annealing were studied. These flakes have a thickness of 80-200 nm, a length of 0.5-10 mu m, and an average grain size of 10-14nm. The addition of some amount of Dy, Nd70Cu30 alloy, and an appropriate post annealing increased the coercivity H-i(c) of the Nd2Fe14B flakes. iHc was 3.7, 4.3, and 5.7 kOe for the Nd15.5Fe78.5B6, Nd14Dy1.5Fe78.5B6 and 83.3wt.% Nd14Dy1.5Fe78.5B6+16.7 wt.% Nd70Cu30 flakes prepared by HEBM for 5 h in heptane with 20 wt.% oleylamine, respectively. After annealing at 450 degrees C for 0.5h, their iHc increased to 5.1, 6.2, and 7.0 kOe, respectively. Anisotropic magnetic behavior was found in all of the as-milled and annealed flakes. Both, the thickening of Nd-rich phase at grain boundaries via diffusion of Nd70Cu30 and the surface modification of the Nd2Fe14B flake could be the main reasons for the coercivity enhancement in the as-milled and annealed Nd70Cu30-added Nd2Fe14B flakes. (C) 2012 American Institute of Physics. [doi: 10.1063/1.3679425]

• Sponsoring Organization: USDOE Advanced Research Projects Agency - Energy (ARPA-E)
• OSTI ID: 1211306
• Journal Information: Journal of Applied Physics, Journal Name: Journal of Applied Physics Journal Issue: 7 Vol. 111; ISSN 0021-8979
• Country of Publication: United States
• Language: English