Ideal CO2/Light Gas Separation Performance of Poly(vinylimidazolium) Membranes and Poly(vinylimidazolium)-Ionic Liquid Composite Films
Six vinyl-based, imidazolium room-temperature ionic liquid (RTIL) monomers were synthesized and photopolymerized to form dense poly(RTIL) membranes. The effect of polymer backbone (i.e., poly(ethylene), poly(styrene), and poly(acrylate)) and functional cationic substituent (e.g., alkyl, fluoroalkyl, oligo(ethylene glycol), and disiloxane) on ideal CO2/N-2 and CO2/CH4 membrane separation performance was investigated. The vinyl-based poly(RTIL)s were found to be generally less CO2-selective compared to analogous styrene- and acrylate-based poly(RTIL)s. The CO2 permeability of n-hexyl-(69 barrers) and disiloxane- (130 barrers) substituted vinyl-based poly(RTIL)s were found to be exceptionally larger than that of previously studied styrene and acrylate poly(RTIL)s. The CO2 selectivity of oligo(ethylene glycol)-functionalized vinyl poly(RTIL)s was enhanced, and the CO2 permeability was reduced when compared to the n-hexyl-substituted vinyl-based poly(RTIL). Nominal improvement in CO2/CH4 selectivity was observed upon fluorination of the n-hexyl vinyl-based poly(RTIL), with no observed change in CO2 permeability. However, rather dramatic improvements in both CO2 permeability and selectivity were observed upon blending 20 mol % RTIL (emim Tf2N) into the n-hexyl- and disiloxane-functionalized vinyl poly(RTIL)s to form solid liquid composite films.
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- DOE Contract Number:
- Grant DE-AR0000098
- OSTI ID:
- 1211148
- Journal Information:
- Industrial and Engineering Chemistry Research, Vol. 52, Issue 3; ISSN 0888-5885
- Country of Publication:
- United States
- Language:
- English
Similar Records
Cross-Linked Poly(ethylene oxide) Ion Gels Containing Functionalized Imidazolium Ionic Liquids as Carbon Dioxide Separation Membranes
Effect of composition and nanostructure on CO2/N-2 transport properties of supported alkyl-imidazolium block copolymer membranes