Magnetic property and microstructure of single crystalline Nd2Fe14B ultrafine particles ball milled from HDDR powders
Journal Article
·
· Journal of Magnetism and Magnetic Materials
In this work we report the microstructure and magnetic property of single crystalline Nd2Fe14B ultrafine particles ball milled from HDDR Nd-Fe-B alloys. The average size of the particles is 283 nm, and TEM observation reveals that these particles are single crystalline. The coercivity of these particles is 6.0 kOe, which is much higher than that of the particles ball milled from sintered and hot pressed Nd-Fe-B magnets. Micromagnetic analysis shows that the coercivity degradation is caused by surface damage during ball milling. (C) 2013 Elsevier B.V. All rights reserved.
- Sponsoring Organization:
- USDOE Advanced Research Projects Agency - Energy (ARPA-E)
- OSTI ID:
- 1211063
- Journal Information:
- Journal of Magnetism and Magnetic Materials, Vol. 339; ISSN 0304-8853
- Country of Publication:
- United States
- Language:
- English
Similar Records
Mechanochemical synthesis of Nd2Fe14B alloy with high coercivity
Single-crystal and textured polycrystalline Nd2Fe14B flakes with a submicron or nanosize thickness
Textured Nd2Fe14B flakes with enhanced coercivity
Journal Article
·
Wed Dec 05 00:00:00 EST 2012
· Journal of Alloys and Compounds
·
OSTI ID:1211063
Single-crystal and textured polycrystalline Nd2Fe14B flakes with a submicron or nanosize thickness
Journal Article
·
Wed Feb 01 00:00:00 EST 2012
· Acta Materialia
·
OSTI ID:1211063
+2 more
Textured Nd2Fe14B flakes with enhanced coercivity
Journal Article
·
Sun Apr 01 00:00:00 EDT 2012
· Journal of Applied Physics
·
OSTI ID:1211063
+2 more