Saturation curve of SiO[subscript 2] component in rutile-type GeO[subscript 2]: A recoverable high-temperature pressure standard from 3 GPa to 10 GPa
Journal Article
·
· J. Solid State Chem.
- AZU
- Research Organization:
- Argonne National Lab. (ANL), Argonne, IL (United States). Advanced Photon Source (APS)
- Sponsoring Organization:
- National Science Foundation (NSF)
- OSTI ID:
- 1184872
- Journal Information:
- J. Solid State Chem., Vol. 229, Issue 09, 2015
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Saturation curve of SiO{sub 2} component in rutile-type GeO{sub 2}: A recoverable high-temperature pressure standard from 3 GPa to 10 GPa
Saturation curve of SiO2 component in rutile-type GeO2: A recoverable high-temperature pressure standard from 3 GPa to 10 GPa
NaEu[subscript 3](GeO[subscript 4])[subscript 2](OH)[subscript 2]: A High-Pressure-Stable Photoluminescent Lanthanide Germanate
Journal Article
·
Tue Sep 15 00:00:00 EDT 2015
· Journal of Solid State Chemistry
·
OSTI ID:1184872
+1 more
Saturation curve of SiO2 component in rutile-type GeO2: A recoverable high-temperature pressure standard from 3 GPa to 10 GPa
Journal Article
·
Tue Sep 01 00:00:00 EDT 2015
· Journal of Solid State Chemistry
·
OSTI ID:1184872
+1 more
NaEu[subscript 3](GeO[subscript 4])[subscript 2](OH)[subscript 2]: A High-Pressure-Stable Photoluminescent Lanthanide Germanate
Journal Article
·
Mon Nov 26 00:00:00 EST 2012
· Eur. J. Inorg. Chem.
·
OSTI ID:1184872
+4 more