UCSB ATR-NSUF Irradiation DMC Sample Inspection Report
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
A variety of tensile samples of Ferritic and Oxide Dispersion Strengthened (ODS or nanoferritic) steels were placed the ATR reactor over 2 Years achieving doses of roughly 4-6 dpa at temperatures of roughly 290°C. After irradiation, samples were shipped from the MFC hot cells at Idaho National Laboratory (INL) to the Wing 9 hot cells in the CMR facility at Los Alamos National Laboratory. Samples were cleaned to removed alpha contamination from the MFC hot cells, and then, as needed removed from their irradiation containers, sorted and inspected. This report will summarize the inspection of the Disc Multipurpose Coupon (DMC) inspection from packet 7-1.
- Research Organization:
- Los Alamos National Lab. (LANL), Los Alamos, NM (United States)
- Sponsoring Organization:
- USDOE National Nuclear Security Administration (NNSA)
- DOE Contract Number:
- AC52-06NA25396
- OSTI ID:
- 1170627
- Report Number(s):
- LA-UR-15-20825
- Country of Publication:
- United States
- Language:
- English
Similar Records
High Temperature Mechanical Properties, Fractography and Synchrotron Studies of ATF clad materials from the UCSB-NSUF Irradiations.
Shear Punch Testing on ATR Irradiated MA956 FeCrAl Alloy
NSUF BRR Cask Shipment Summary Report
Technical Report
·
Sun Feb 22 23:00:00 EST 2015
·
OSTI ID:1170626
Shear Punch Testing on ATR Irradiated MA956 FeCrAl Alloy
Technical Report
·
Tue Jun 13 00:00:00 EDT 2017
·
OSTI ID:1363743
NSUF BRR Cask Shipment Summary Report
Program Document
·
Fri Oct 01 00:00:00 EDT 2021
·
OSTI ID:1823477