The Effect of Braze Interlayer Thickness on the Mechanical Strength of Alumina Brazed with Ag-CuO Braze Alloys

Journal Article · Sun Nov 30 23:00:00 EST 2014 · Advanced Engineering Materials, 16(12):1442-1447

DOI:https://doi.org/10.1002/adem.201400128· OSTI ID:1170071

Erskine, Kevin M.; Meier, Alan; Joshi, Vineet V.; Pilgrim, Steven M.

The effect of braze interlayer thickness on the strength of alumina brazed with silver-copper oxide reactive air braze (RAB) alloys was evaluated using a four point bend test configuration. The brazed samples had an average fracture strength of 180 MPa or approximately 60 percent of the average monolithic alumina strength. The joint strength values obtained exceeded the yield strength and ultimate tensile strength of the silver interlayer indicating strong ceramic to metal adhesion and the development of a triaxial stress state in the braze interlayer. The average fracture strength was relatively constant (190 ± 60 MPa) in the thickness range of 0.030 mm to 0.230 mm for all test conditions. The braze fracture strength then decreased down to 100 ± 30 MPa as the braze thickness increased from 0.230 mm to 0.430 mm indicating a loss of triaxial constraint with increasing interlayer thickness. In addition, four different fracture modes were observed.

• Research Organization: Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
• Sponsoring Organization: USDOE
• DOE Contract Number: AC05-76RL01830
• OSTI ID: 1170071
• Report Number(s): PNNL-SA-101968; AA6010000
• Journal Information: Advanced Engineering Materials, 16(12):1442-1447, Journal Name: Advanced Engineering Materials, 16(12):1442-1447
• Country of Publication: United States
• Language: English