Efficient Polymer Solar Cells Fabricated on Poly(3,4-ethylenedioxythiophene):Poly(styrenesulfonate)-Etched Old Indium Tin Oxide Substrates
- Mansoura University
- Ames Laboratory
In organic electronic devices, indium tin oxide (ITO) and poly(3,4-ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS) are the most common transparent electrode and anodic buffer layer materials, respectively. A widespread concern is that PEDOT:PSS is acidic and etches ITO. We show that this issue is not serious: only a few nanometers of ITO are etched in typical device processing conditions and storage thereafter; conductivity losses are affordable; and optical transmission gains further offset these losses. Organic photovoltaic (OPV) devices fabricated on old ITO (with PEDOT:PSS history) were similar or higher in efficiency than devices on fresh ITO. Poly[[4,8-bis[(2-ethylhexyl)oxy]benzo[1,2-b:4,5-b']dithiophene-2,6-diyl][3-fluoro-2-[(2-ethylhexyl)carbonyl]thieno[3,4-b]thiophenediyl]] (PTB7) devices on old ITO showed efficiencies up to 9.24% compared to 8.72% efficient devices on fresh ITO. This reusability of ITO can be impactful for economics of organic electronics because ITO accounts for almost 90% of energy embedded in devices, such as OPVs.
- Research Organization:
- Ames Lab., Ames, IA (United States)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC02-07CH11358
- OSTI ID:
- 1163925
- Report Number(s):
- IS-J 8436
- Journal Information:
- ACS Applied Materials and Interfaces, Vol. 6, Issue 15; ISSN 1944-8244
- Publisher:
- American Chemical Society
- Country of Publication:
- United States
- Language:
- English
Similar Records
Is organic photovoltaics promising for indoor applications?
Quantitative comparison of organic photovoltaic bulk heterojunction photostability under laser illumination