A comparative evaluation of laser and GTA welds in a high-strength titanium alloy -- Ti-6-22-22S
- and others
Titanium alloy Ti-6Al-2Sn-2Zr-2Mo-2Cr-025Si (hereafter designated Ti-6-22-22S)is an alpha-beta titanium alloy developed for deep hardenability, high strength, intermediate temperature creep resistance, and moderate toughness. As a potential structural material for next-generation aircraft and aerospace systems, the weldability of Ti-6-22-22S has recently become a subject of increasing importance and concern. In the welding of titanium sheet, achieving satisfactory ductility is the principal limitation to alloy weldability, with poor ductility promoted by a coarse beta grain structure in the weld fusion and near-heat-affected zones. Square-butt welds were produced in 1.6 mm thick Ti-6-22-22S sheet using automatic GTA and CO{sub 2} laser welding systems. Microstructure analysis and DPH hardness traverses were performed on mounted. polished and etched specimens. Three-point bend and tensile tests were performed on transverse-weld and longitudinal-weld oriented specimens. Microstructure analysis of the laser welds revealed a fine, columnar fusion zone beta grain macrostructure and a fully-martensitic transformed-beta microstructure. Consistent with the microstructural similarities, fusion zone hardnesses of the laser welds were comparable (385 and 390 DPG, respectively) and greater than that of the base metal (330 DPH). In general, laser welds did not exhibit markedly superior ductilities relative to the GTAW, which was attributed to differences in the nature of the intragranular transformed-beta microstructures, being coarser and softer for the GTAW, the response of these as-welded microstructures to heat treatment, and interactions between the transformed-beta microstructure and the beta grain macrostructure.
- OSTI ID:
- 115480
- Report Number(s):
- CONF-9404233-; TRN: 95:002927-0058
- Resource Relation:
- Conference: 75. American Welding Society (AWS) annual meeting, Philadelphia, PA (United States), 10-15 Apr 1994; Other Information: PBD: 1994; Related Information: Is Part Of 75th Diamond anniversary American Welding Society annual meeting; PB: 273 p.
- Country of Publication:
- United States
- Language:
- English
Similar Records
Cooling rate effects in Ti-6Al-2Sn-4Zr-2Mo weldments
An evaluation of CO[sub 2] laser beam welding on a Ti[sub 3]Al-Nb alloy