Transport and magnetism correlations in thin-film ferromagnetic oxides
In order to determine the {Tc}-dependence of the colossal magnetoresistance (MR) exhibited by the ferromagnetic La{sub 0.7}M{sub 0.3}MnO{sub 3+{sigma}} (M = Ba, Ca, Sr) system, the authors examine the magnetic-field and temperature dependent resistivity and magnetization of a series of thin films that were grown via pulsed-laser deposition. The films had magnetic ordering temperatures (T{sub C}) ranging from 150 to 350 K; all samples displayed a large negative MR that is largest near {Tc}. The magnitude of a given sample`s MR at {Tc} inversely correlates with {Tc}; samples with a low {Tc} display significantly larger MR values than do samples with large {Tc}`s. The quantity {rho}({Tc})/{rho}(4 K), the amount by which the resistivity is reduced by full ferromagnetic order, is an activated function of {Tc} with an activation energy E{sub a} = 0.1 eV. These results indicate that the magnitude of the CMR effect in a given specimen is controlled not by {rho}({Tc}), but by {Tc} via the ratio {rho}({Tc})/{rho}(4 K). Phenomenological scaling relationships are also reported that link {rho}(H,T) to both H and M(H, T).
- Research Organization:
- Los Alamos National Lab., NM (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-7405-ENG-36
- OSTI ID:
- 113963
- Report Number(s):
- LA-UR--95-3027; CONF-951101--4; ON: DE96000069
- Country of Publication:
- United States
- Language:
- English
Similar Records
Magnetotransport in perovskite series La{sub n{minus}nx}Ca{sub 1+nx}Mn{sub n}O{sub 3n+1} ferromagnets
Interplay between electronic transport and magnetic order in ferromagnetic magnetic manganite thin films