Ultrasonic Detection of Delamination and Material Characterization of Thermal Barrier Coatings
This article describes ultrasonic nondestructive evaluation (NDE) to detect the changes of material properties and provide early warning of delamination in thermal barrier coating (TBC) systems. NDE tests were performed on single-crystal René N5 superalloy coupons that were coated with a commercially available MCrAlY bond coat and an air plasma sprayed 7% yttria-stabilized zirconia (YSZ) top coat deposited by Air Plasma Spray method, as well as Haynes 230 superalloy coupons coated with MCrA1Y bond coat, and an electron beam physical vapor deposit of 7% YSZ top coat. The TBC coupons were subjected to either cyclic or isothermal exposure for various lengths of time at temperatures ranging from 900 to 1100 °C. The ultrasonic measurements performed on the coupons had provided an early warning of delamination along the top coat/TGO interface before exposure time, when delamination occurred. The material's property (Young’s modulus) of the top coat was estimated using the measured wave speeds. Finite element analysis (FEA) of the ultrasonic wave propagation was conducted on a simplified TBC system to verify experimental observations. The technique developed was also demonstrated on an as-manufactured turbine blade to estimate normalized top coat thickness measurements.
- Research Organization:
- National Energy Technology Lab. (NETL), Pittsburgh, PA, and Morgantown, WV (United States). In-house Research
- Sponsoring Organization:
- USDOE Office of Fossil Energy (FE)
- DOE Contract Number:
- DE-FE0004000
- OSTI ID:
- 1129539
- Report Number(s):
- A-UNIV-PUB-028
- Journal Information:
- JOURNAL OF THERMAL SPRAY TECHNOLOGY, Vol. 21, Issue 6
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of higher water vapor content on TBC performance
NON-DESTRUCTIVE TBC SPALLATION DETECTION BY A MICRO-INDENTATION METHOD