Interaction Studies of Ceramic Vacuum Plasma Spraying for the Melting Crucible Materials
Candidate coating materials for re-usable metallic nuclear fuel crucibles, TaC, TiC, ZrC, ZrO2, and Y2O3, were plasmasprayed onto a niobium substrate. The microstructure of the plasma-sprayed coatings and thermal cycling behavior were characterized, and U-Zr melt interaction studies were carried out. The TaC and Y2O3 coating layers had a uniform thickness, and high density with only a few small closed pores showing good consolidation, while the ZrC, TiC, and ZrO2 coatings were not well consolidated with a considerable amount of porosity. Thermal cycling tests showed that the adhesion of the TiC, ZrC, and ZrO2 coating layers with niobium was relatively weak compared to the TaC and Y2O3 coatings. The TaC and Y2O3 coatings had better cycling characteristics with no interconnected cracks. In the interaction studies, ZrC and ZrO2 coated rods showed significant degradations after exposure to U-10 wt.% Zr melt at 1600 degrees C for 15 min., but TaC, TiC, and Y2O3 coatings showed good compatibility with U-Zr melt.
- Research Organization:
- Idaho National Lab. (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- DE-AC07-05ID14517
- OSTI ID:
- 1120805
- Report Number(s):
- INL/JOU-14-31285
- Journal Information:
- Nuclear Engineering and Technology, Vol. 45, Issue 5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Ceramic plasma-sprayed coating of melting crucibles for casting metal fuel slugs
Assessment of ceramic coatings for metal fuel melting crucible