Fabrication and characterization of oxide fibrous monoliths produced by coextrusion.
Conference
·
OSTI ID:11176
Unidirectional fibrous monoliths (FMs) based on dense, strong ZrSiO{sub 4} cells that were surrounded by a porous, weaker ZrSiO{sub 4} cell-boundary phase were fabricated. A duplex filament was coextruded, sectioned, bundled, and the resulting bundle was extruded to form a new filament. This filament was cut and packed into plate and bar dies to produce FM test specimens. Four-point flexural tests were conducted on the cell material, cell-boundary material, and FMs. After testing, fracture surfaces and cross sections were examined by scanning electron microscopy. The FMs exhibited graceful failure in flexural testing, and the fracture surfaces exhibited clear evidence of crack deflection and delamination.
- Research Organization:
- Argonne National Lab., IL (US)
- Sponsoring Organization:
- US Department of Energy (US)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 11176
- Report Number(s):
- ANL/ET/CP-97898
- Country of Publication:
- United States
- Language:
- English
Similar Records
Fabrication and characterization of a porous-matrix oxide fibrous monoliths.
A comparison study of the processing methods and properties for zirconium silicate fibrous monoliths.
SiC and Si{sub 3}N{sub 4} fibrous monoliths: Non-brittle fracture from powder processed ceramics produced by coextrusion
Conference
·
Mon Mar 01 23:00:00 EST 1999
·
OSTI ID:10961
A comparison study of the processing methods and properties for zirconium silicate fibrous monoliths.
Conference
·
Fri Dec 31 23:00:00 EST 1999
·
OSTI ID:917683
SiC and Si{sub 3}N{sub 4} fibrous monoliths: Non-brittle fracture from powder processed ceramics produced by coextrusion
Conference
·
Fri Sep 01 00:00:00 EDT 1995
·
OSTI ID:99180