THE EFFECT OF TEMPERATURE AND UNIAXIAL PRESSURE ON THE DENSIFICATION BEHAVIOR OF SILICA AEROGEL GRANULES
Materials are being developed in U.S. for the removal and immobilization of iodine from gaseous products of nuclear fuel reprocessing in support of the Fuel Cycle Technology Separations and Waste Forms Campaign. The silver-functionalized silica aerogel proved to be an excellent candidate for this treatment because of its high selectivity and sorption capacity for radioiodine and its possible conversion to a durable silica-based waste form. The present study investigated with nitrogen sorption and helium pycnometry the effect of pressureless isothermal sintering at temperatures of 900-1400°C for 2.5-90 min or isothermal hot-pressing at 1200°C for 2.5 min on densification of raw and silver-functionalized silica aerogel granules. Rapid sintering was observed at 1050 and 1200°C. Only 15 min of pressureless sintering at 1200°C resulted in almost complete densification. The macropores disappeared, surface area decreased from 1114 m2/g to 25 m2/g, pore volume from 7.41 cm3/g to 0.09 cm3/g, and adsorption pore size from 18.7 to 7 nm. The skeletal density of sintered granules was similar to the bulk density of amorphous silica (2.2 g/cm3). The hot-pressing accelerated the sintering process, decreasing significantly the pore size and volume.
- Research Organization:
- Pacific Northwest National Laboratory (PNNL), Richland, WA (US)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1113617
- Report Number(s):
- PNNL-SA-85797; AF5805000
- Country of Publication:
- United States
- Language:
- English
Similar Records
The role of additives in the densification of nitrogen ceramics. Annual report no. 2 (final)
Densification of nano-size powders. 1994 report