Corrosion of high temperature alloys in solar salt at 400, 500, and 680ÀC.

Technical Report · Sun Sep 01 04:00:00 EDT 2013

DOI:https://doi.org/10.2172/1104752· OSTI ID:1104752

Kruizenga, Alan Michael; Gill, David Dennis; LaFord, Marianne Elizabeth

Corrosion tests at 400, 500, and 680ÀC were performed using four high temperature alloys; 347SS, 321SS In625, and HA230. Molten salt chemistry was monitored over time through analysis of nitrite, carbonate, and dissolved metals. Metallography was performed on alloys at 500 and 680ÀC, due to the relatively thin oxide scale observed at 400ÀC. At 500ÀC, corrosion of iron based alloys took the form of chromium depletion and iron oxides, while nickel based alloys also had chromium depletion and formation of NiO. Chromium was detected in relatively low concentrations at this temperature. At 680ÀC, significant surface corrosion occurred with metal losses greater than 450microns/year after 1025hours of exposure. Iron based alloys formed complex iron, sodium, and chromium oxides. Some data suggests grain boundary chromium depletion of 321SS. Nickel alloys formed NiO and metallic nickel corrosion morphologies, with HA230 displaying significant internal oxidation in the form of chromia. Nickel alloys both exhibited worse corrosion than iron based alloys likely due to preferential dissolution of chromium, molybdenum, and tungsten.

• Research Organization: Sandia National Laboratories (SNL-CA), Livermore, CA (United States)
• Sponsoring Organization: USDOE National Nuclear Security Administration (NNSA)
• DOE Contract Number: AC04-94AL85000
• OSTI ID: 1104752
• Report Number(s): SAND2013-8256; 477131
• Country of Publication: United States
• Language: English