Development and Test Evaluations for Ni-DOBDC Metal Organic Framework (MOF) Engineered Forms
- Idaho National Laboratory (INL), Idaho Falls, ID (United States)
- Pacific Northwest National Laboratory (PNNL), Richland, WA (United States)
- Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)
A joint effort to prepare engineered forms of a Ni-DOBDC metal organic framework (MOF) was completed with contributions from PNNL, SNL and the INL. Two independent methods were used at INL and SNL to prepare engineered form (EF) sorbents from Ni-DOBDC MOF powder developed and prepared at PNNL. Xe and Kr capacity test evaluations were performed at ambient temperature with the cryostat experimental setup at INL. The initial INL EF MOF test results indicated a Xe capacity of 1.6 mmol/kg sorbent and no Kr capacity. A large loss of surface area also occurred during minimal testing rendering the INL EF MOF unusable. Four capacity tests were completed using the SNL EF MOF at ambient temperature and resulted in Xe capacities of 1.4, 4.2, 5.0 and 3.8 mmol/kg sorbent with no Kr capacity observed in any ambient temperature tests. Two additional capacity tests were performed at 240 K to further evaluate SNL EF MOF performance. Xe capacities of 50.7 and 49.3 mmol/kg of sorbent and Kr capacities of 0.77 and 0.69 mmol/kg of sorbent were obtained, respectively. Following the adsorption evaluations, the SNL EF MOF material had lost about 40 % of the initial mass and 40 % of the initial surface area. In general, the Xe capacity results at ambient temperature for the INL and SNL EF Ni-DOBDC MOF’s were lower than 9.8 mmol Xe/kg sorbent test results reported by INL in FY-12 using PNNL’s inital EF supplied material.
- Research Organization:
- Idaho National Laboratory (INL), Idaho Falls, ID (United States)
- Sponsoring Organization:
- USDOE Office of Nuclear Energy (NE)
- DOE Contract Number:
- AC07-05ID14517
- OSTI ID:
- 1097148
- Report Number(s):
- INL/EXT--13-29706; FCR&D-SWF-2013-000227
- Country of Publication:
- United States
- Language:
- English
Similar Records
Evaluation of an Engineered Form MOF CaSDB
Pressure Swing and Thermal Swing Capacity Comparison for Kr and Xe using AgZ-PAN and HZ-PAN Sorbents
Initial Evaluation of CaSDB MOF Xe and Kr Capacities
Technical Report
·
Mon Jul 08 00:00:00 EDT 2019
·
OSTI ID:1542584
Pressure Swing and Thermal Swing Capacity Comparison for Kr and Xe using AgZ-PAN and HZ-PAN Sorbents
Technical Report
·
Tue Aug 27 00:00:00 EDT 2013
·
OSTI ID:1107268
Initial Evaluation of CaSDB MOF Xe and Kr Capacities
Technical Report
·
Fri Mar 30 00:00:00 EDT 2018
·
OSTI ID:1467472