Characterization and Analyses of Degradation and Recovery of LaNi4.78Sn0.22 Hydrides Following Thermal Aging
- ORNL
- Jet Propulsion Laboratory, Pasadena, CA
- Eindhoven University of Technology
LaNi4.78Sn0.22Hx hydride samples were held at a hydrogen content of x > 5.0 (x is H/La atomic ratio) and temperatures above 465 K to accelerate the intrinsic degradation processes. Although Sn-substituted alloys are much more resistant to disproportionation than nearly all other LaNi5 alloys, the present test conditions did produce substantial degradation. Effects observed included reduction in hydrogen storage capacity, decreases in the plateau pressures, increased slopes of the plateaus, and smaller hysteresis ratios. A regeneration process nearly completely restored the behavior of the degraded LaNi4.78Sn0.22 hydride to its initial value. First-principles chemical reaction kinetics and statistical thermodynamics simulations have replicated experimental pressure-composition hydrogen gas absorption isotherms for both initial and degraded LaNi4.78Sn0.22 hydride. Neutron diffraction characterization of phase compositions, crystal structures, and hydrogen content have been performed on undamaged, degraded, and regenerated LaNi4.78Sn0.22 deuterides.
- Research Organization:
- Oak Ridge National Laboratory (ORNL); Spallation Neutron Source
- Sponsoring Organization:
- SC USDOE - Office of Science (SC)
- DOE Contract Number:
- AC05-00OR22725
- OSTI ID:
- 1096964
- Country of Publication:
- United States
- Language:
- English
Similar Records
Predictive criteria for low-hysteresis metal hydrides (materials research). Final report on Phase, 1 January-July 1984
Interface pinning causes the hysteresis of the hydride transformation in binary metal hydrides