Grain orientation dependence of lattice strains and intergranular damage rates in polycrystals under cyclic loading
Journal Article
·
· Scripta Materialia
- University of Tennessee, Knoxville (UTK)
- University of Tennessee, Knoxville (UTK) & Oak Ridge National Laboratory (ORNL)
- Beijing Institute of Technology, Beijing
- ORNL
- Research Organization:
- Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States). Spallation Neutron Source (SNS)
- Sponsoring Organization:
- USDOE Office of Science (SC)
- DOE Contract Number:
- DE-AC05-00OR22725
- OSTI ID:
- 1069344
- Journal Information:
- Scripta Materialia, Vol. 68, Issue 5; ISSN 1359-6462
- Country of Publication:
- United States
- Language:
- English
Similar Records
Grain Orientation Dependence of the Residual Lattice Strain in a Cold Rolled Interstitial-Free Steel
Cyclic-loading Induced Lattice-Strain Asymmetry in Loading and Transverse Directions
Fracture of Ni with grain-size from nanocrystalline to ultrafine scale under cyclic loading
Journal Article
·
Wed Jan 10 00:00:00 EST 2018
· Steel Research International
·
OSTI ID:1069344
+5 more
Cyclic-loading Induced Lattice-Strain Asymmetry in Loading and Transverse Directions
Journal Article
·
Sun Jan 01 00:00:00 EST 2012
· Metallurgical and Materials Transactions A
·
OSTI ID:1069344
+1 more
Fracture of Ni with grain-size from nanocrystalline to ultrafine scale under cyclic loading
Journal Article
·
Mon Jan 01 00:00:00 EST 2007
· Scripta Materialia
·
OSTI ID:1069344
+3 more