Nondestructive Characterization of Aged Components

Technical Report · Tue Oct 21 00:00:00 EDT 2003

DOI:https://doi.org/10.2172/1069219· OSTI ID:1069219

Panetta, Paul D; Toloczko, Mychailo B; Garner, Francis A; Balachov, Iouri I

It is known that high energy radiation can have numerous effects on materials. In metals and alloys, the effects include, but may not be limited to, mechanical property changes, physical property changes, compositional changes, phase changes, and dimensional changes. Metals and alloys which undergo high energy self-irradiation are also susceptible to these changes. One of the greatest concerns with irradiation of materials is the phenomenon of void swelling which has been observed in a wide variety of metals and alloys. Irradiation causes the formation of a high concentration point defects and microclusters of vacancies and interstitials. With the assistance of an inert atom such as helium, the vacancy-type defects can coalesce to form a stable bubble. This bubble will continue to grow through the net absorption of more vacancy-type defects and helium atoms, and upon reaching a certain critical size, the bubble will begin to grow at an accelerated rate without the assistance of inert atom absorption. The bubble is then said to be an unstably growing void. Depending on the alloy system and environment, swelling values can reach in excess of 50% !V/Vo where Vo is the initial volume of the material. Along with dimensional changes resulting from the formation of bubbles and voids comes changes in the macroscopically observed speed of sound, moduli, electrical resistivity, yield strength, and other properties. These effects can be detrimental to the designed operation of the aged components. In situations where irradiation has sufficient time to cause degradation to materials used in critical applications such as nuclear reactor core structural materials, it is advisable to regularly survey the material properties. It is common practice to use surveillance specimens, but this is not always possible. When surveillance materials are not available, other means for surveying the material properties must be utilized. Sometimes it is possible to core out a small sample which may be used for material properties measurements. A more appealing solution is to use nondestructive evaluation (NDE) methods.

• Research Organization: Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
• Sponsoring Organization: USDOE
• DOE Contract Number: AC05-76RL01830
• OSTI ID: 1069219
• Report Number(s): PNNL-14471
• Country of Publication: United States
• Language: English