Replicated mask surface roughness effects on EUV lithographic pattering and line edge roughness
To quantify the roughness contributions to speckle, a programmed roughness substrate was fabricated with a number of areas having different roughness magnitudes. The substrate was then multilayer coated. Atomic force microscopy (AFM) surface maps were collected before and after multilayer deposition. At-wavelength reflectance and total integrated scattering measurements were also completed. Angle resolved scattering based power spectral densities are directly compared to the AFM based power spectra. We show that AFM overpredicts the roughness in the picometer measurements range. The mask was then imaged at-wavelength for the direct characterization of the aerial image speckle using the SEMATECH Berkeley Actinic Inspection Tool (AIT). Modeling was used to test the effectiveness of the different metrologies in predicting the measured aerial-image speckle. AIT measured contrast values are 25% or more than the calculated image contrast values obtained using the measured rms roughness input. The extent to which the various metrologies can be utilized for specifying tolerable roughness limits on EUV masks is still to be determined. Further modeling and measurements are being planned.
- Research Organization:
- Lawrence Berkeley National Lab. (LBNL), Berkeley, CA (United States)
- Sponsoring Organization:
- Materials Sciences Division
- DOE Contract Number:
- DE-AC02-05CH11231
- OSTI ID:
- 1050640
- Report Number(s):
- LBNL-4813E; TRN: US201218%%854
- Resource Relation:
- Conference: SPIE advanced lithography, San Jose, CA, February 27 - March 3, 2011
- Country of Publication:
- United States
- Language:
- English
Similar Records
Actinic EUV mask inspection beyond 0.25 NA
Evaluating EUV mask pattern imaging with two EUV microscopes