The use Na, Li, K cations for modification of ZSM-5 zewolite to control hydrocarbon cold-start emission
This paper addresses the problem of controlling hydrocarbon emissions from cold-start of engines by investigating the adsorbents which could adsorb the hydrocarbons at cold temperatures and hold them to 250-300 ?. The materials, that has been studied, are based on the modification of ZSM-5 (SiO{sub 2}/Al{sub 2}O{sub 3} = 35) zeolite with Li, K, Na cations. It has been shown that the introduction of Li, Na and K in an amount that is equivalent to the content of Al in zeolite results in occurrence of toluene temperature desorption peaks at high-temperatures. The toluene temperature desorption curves for 5%Li-ZSM-5 and 2.3%Na-ZSM-5 zeolites are identical and have peak toluene desorption rate between 200 to 400 ?. Upon analysis of toluene adsorption isotherms for 2.3%Na-ZSM-5 and 5%Li-ZSM-5, it was concluded that the toluene diffusion inside of the modified zeolites channels is extremely slow and the sorption capacity of 2.3%Na-ZSM-5 is higher than with 5%Li-ZSM-5. The 2.3%Na-ZSM-5 didn't change toluene temperature programmed desorption (TPD) rate of curve after the treatment in environment with 10% ?{sub 2}? at 750-800 ? for about 28 h. The 2.3%Na-ZSM-5 zeolite is very promising as adsorbent to control the cold-start hydrocarbon emissions.
- Research Organization:
- BROOKHAVEN NATIONAL LABORATORY (BNL)
- Sponsoring Organization:
- USDOE NA NATIONAL NUCLEAR SECURITY ADMINISTRATION (NNSA)
- DOE Contract Number:
- AC02-98CH10886
- OSTI ID:
- 1044763
- Report Number(s):
- BNL--98040-2012-CP; NN4006010
- Country of Publication:
- United States
- Language:
- English
Similar Records
Reactor trap to remove hydrocarbons from engine exhaust during cold start
Acidity and catalytic properties of H-Na-ZSM-8 zeolite: effect of H/sup +/ exchange, pretreatment condition, and poisoning of stronger acid sites