Platinum Monolayer on IrFe Core-Shell Nanoparticle Electrocatalysts for the Oxygen Reduction Reaction
We synthesized high activity and stability platinum monolayer on IrFe core-shell nanoparticle electrocatalysts. Carbon-supported IrFe core-shell nanoparticles were synthesized by chemical reduction and subsequent thermal annealing. The formation of Ir shells on IrFe solid-solution alloy cores has been verified by scanning transmission electron microscopy coupled with energy-loss spectroscopy (EELS) and in situ X-ray absorption spectroscopy. The Pt monolayers were deposited on IrFe core-shell nanoparticles by galvanic replacement of underpotentially deposited Cu adatoms on the Ir shell surfaces. The specific and Pt mass activities for the ORR on the Pt monolayer on IrFe core-shell nanoparticle electrocatalyst are 0.46 mA/cm{sup 2} and 1.1 A/mg{sub Pt}, which are much higher than those on a commercial Pt/C electrocatalyst. High durability of Pt{sub ML}/IrFe/C has also been demonstrated by potential cycling tests. These high activity and durability observed can be ascribed to the structural and electronic interaction between the Pt monolayer and the IrFe core-shell nanoparticles.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States)
- Sponsoring Organization:
- USDOE SC OFFICE OF SCIENCE (SC)
- DOE Contract Number:
- DE-AC02-98CH10886
- OSTI ID:
- 1042335
- Report Number(s):
- BNL-98013-2012-JA; TRN: US201212%%745
- Journal Information:
- Electrocatalysis, Vol. 2, Issue 2; ISSN 1868-2529
- Country of Publication:
- United States
- Language:
- English
Similar Records
Platinum Monolayer on Nonnoble Metal-Nobel Metal Core-Shell Nanoparticle Electrocatalysts for O2 Reduction
Synthesis and Characterization of Platinum Monolayer Oxygen-Reduction Electrocatalysts with Co-Pd Core-Shell Nanoparticle Support
Related Subjects
ORGANIC
PHYSICAL AND ANALYTICAL CHEMISTRY
ABSORPTION SPECTROSCOPY
ALLOYS
ANNEALING
CARBON
CATALYST SUPPORTS
DEPOSITION
ELECTROCATALYSTS
ENERGY-LOSS SPECTROSCOPY
INTERACTIONS
IRIDIUM
IRON
LAYERS
OXYGEN
PLATINUM
REDUCTION
STABILITY
SURFACES
TRANSMISSION ELECTRON MICROSCOPY
X-RAY DIFFRACTION