Microscopic Dynamics in Nanocomposite Photosensitive Films Studies by X-ray Photon Correlation Spectroscopy
X-ray photon correlation spectroscopy measurements are reported of microscale dynamics in Langmuir-Schaeffer deposited multilayers of a photosensitive azopolymer with a low concentration of gold nanoparticles embedded. Correlation functions were measured as a function of exchanged momentum and illumination conditions (dark and UV light) and fitted with the Kohlrausch-Williams-Watts (KWW) exponential form. The microscopic dynamic of the nanoparticles was quantified, evidencing a non-Brownian superdiffusive behavior with relaxation times {tau} {approx} q{sup -1}, a result analogous to what previously had been observed in the pure azopolymer. Such behavior has been related to intermittent rearrangements or random dipolar interactions within an elastic medium. Photoperturbation with UV light makes the dynamics faster, in accordance with the reduction of the viscosity of the polymer found by shear rheology, but the KWW form of the correlation functions persists. At constant temperature, the dynamics of the nanoparticles embedded in the polymeric matrix is sensibly faster than the slow microscopic dynamic of the polymer. At the same time, the Vogel-Fulcher-Tammann law for the relaxation times indicates a less pronounced temperature dependence than for the pure polymer, resulting in a slightly lower activation temperature T{sub A}.
- Research Organization:
- BROOKHAVEN NATIONAL LABORATORY (BNL)
- Sponsoring Organization:
- USDOE SC OFFICE OF SCIENCE (SC)
- DOE Contract Number:
- AC02-98CH10886
- OSTI ID:
- 1042050
- Report Number(s):
- BNL--97728-2012-JA
- Journal Information:
- Philosophical Magazine. A. Structure, defects and mechanical properties, Journal Name: Philosophical Magazine. A. Structure, defects and mechanical properties Journal Issue: 13-15 Vol. 91; ISSN 1478-6435
- Country of Publication:
- United States
- Language:
- English
Similar Records
Supercooled spin liquid state in the frustrated pyrochlore Dy2Ti2O7
Ion conduction and relaxation in PEO-LiTFSI-Al{sub 2}O{sub 3} polymer nanocomposite electrolytes