Cyclic Oxidation Behavior of HVOF Bond Coatings Deposited on La- and Y-doped Superalloys

Conference · Sat Jan 01 04:00:00 EST 2011

OSTI ID:1030615

Pint, Bruce A ^[1]; Bestor, Michael A ^[1]; Haynes, James A ^[1]

---

1. ORNL

One suggested strategy for improving the performance of thermal barrier coating (TBC) systems used to protect hot section components in gas turbines is the addition of low levels of dopants to the Ni-base superalloy substrate. To quantify the benefit of these dopants, the oxidation behavior of three commercial superalloys with different Y and La contents was evaluated with and without a NiCoCrAlYHfSi bond coating deposited by high velocity oxygen fuel (HVOF) spraying. Cyclic oxidation experiments were conducted in dry O{sub 2} at 1050, 1100 and 1150 C. At the highest temperature, the bare superalloy without La showed more attack due to its lower Al content but no difference in oxidation rate or scale adhesion was noted at lower temperatures. With a bond coating, the alumina scale was non-uniform in thickness and spalled at each temperature. Among the three coated superalloys, no clear difference in oxide growth rate or scale adhesion was observed. Evaluations with a YSZ top coat and a bond coating without Hf are needed to better determine the effect of superalloy dopants on high temperature oxidation performance.

• Research Organization: Oak Ridge National Laboratory (ORNL)
• Sponsoring Organization: FE USDOE - Office of Fossil Energy (FE)
• DOE Contract Number: AC05-00OR22725
• OSTI ID: 1030615
• Country of Publication: United States
• Language: English

Related Subjects

36 MATERIALS SCIENCE
ADHESION
COATINGS
Coatings
GAS TURBINES
HEAT RESISTING ALLOYS
OXIDATION
OXIDES
OXYGEN
PERFORMANCE
THERMAL BARRIERS
THICKNESS
THIN FILMS
VELOCITY
alloy dopants
oxidation
superalloy
thermal spray