Secondary Waste Form Down-Selection Data Package—DuraLith
This data package developed for the DuraLith wasteform includes information available in the open literature and from data obtained from testing currently underway. DuraLith is an alkali-activated geopolymer waste form developed by the Vitreous State Laboratory at The Catholic University of America (VSL-CUA) for encapsulating liquid radioactive waste. A DuraLith waste form developed for treating Hanford secondary waste liquids is prepared by alkali-activation of a mixture of ground blast furnace slag and metakaolinite with sand used as a filler material. Based on optimization tests, solid waste loading of {approx}7.5% and {approx}14.7 % has been achieved using the Hanford secondary waste S1 and S4 simulants, respectively. The Na loading in both cases is equivalent to {approx}6 M. Some of the critical parameters for the DuraLith process include, hydrogen generation and heat evolution during activator solution preparation using the waste simulant, heat evolution during and after mixing the activator solution with the dry ingredients, and a working window of {approx}20 minutes to complete the pouring of the DuraLith mixture into molds. Results of the most recent testing indicated that the working window can be extended to {approx}30 minutes if 75 wt% of the binder components, namely, blast furnace slag and metakaolin are replaced by Class F fly ash. A preliminary DuraLith process flow sheet developed by VSL-CUA for processing Hanford secondary waste indicated that 10 to 22 waste monoliths (each 48 ft3 in volume) can be produced per day. There are no current pilot-scale or full-scale DuraLith plants under construction or in operation; therefore, the cost of DuraLith production is unknown. The results of the non-regulatory leach tests, EPA Draft 1313 and 1316, Waste Simulant S1-optimized DuraLith specimens indicated that the concentrations of RCRA metals (Ag, Cd, Cr, Hg, and Pb) in the leachates were well below the Universal Treatment Standard limits in 40 CFR 268.48. The data from the EPA draft 1315 leach test showed that LI values for COCs, namely 99Tc and I, ranged from 8.2 to 11.4 and 4.3 to 7.5, respectively. These values indicate that 99Tc meets the WAC LI requirement of 9.0 whereas, the LI values for I does not meet the WAC requirement of 11.0. Results of Toxicity Characteristic Leaching Procedure (TCLP)(EPA Method 1311) conducted on Waste Simulant S1-optimized DuraLith specimens, indicated that the concentrations of RCRA metals (Ag, As, Cd, Cr, Hg, and Pb) in the leachates were well below the Universal Treatment Standard limits in 40 CFR 268.48. The data from the ANSI/ANS 16.1 leach test showed that LI values for COC, namely Re (as a Tc surrogate), ranged from 8.06 to 10.81. The LI value for another COC, namely I, was not measured in this test. The results of the compressive strength testing of Waste Simulant S1-optimized DuraLith specimens indicated that the monoliths were physically robust with compressive strengths ranging from 115.5 MPa (16757 psi) to 156.2 MPA (22667 psi).
- Research Organization:
- Pacific Northwest National Lab. (PNNL), Richland, WA (United States)
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC05-76RL01830
- OSTI ID:
- 1027184
- Report Number(s):
- PNNL-20718; 830403000; TRN: US1105689
- Country of Publication:
- United States
- Language:
- English
Similar Records
Off-Gas Condensate and Cast Stone Analysis Results
Tank Waste LDR Organics Data Summary for Sample-and-Send (Rev.1A)
Related Subjects
BINDERS
BLAST FURNACES
CONSTRUCTION
FILLERS
FLOWSHEETS
FLY ASH
LEACHATES
LEACHING
MIXTURES
OPTIMIZATION
RADIOACTIVE WASTES
SAND
SLAGS
SOLID WASTES
TESTING
TOXICITY
US EPA
WASTE FORMS
WASTES
Secondary Waste Form
Down-selection
Duralith