A Novel Synthesis Route for Bimetallic CoCr–MCM-41 Catalysts with Higher Metal Loadings. Their Application in the High Yield, Selective Synthesis of Single-Wall Carbon Nanotubes
We present a study on CoCr-MCM-41 catalysts with stable nm-sized particles. The focus is their promoting effect on the synthesis of Single-Wall Carbon Nanotubes (SWNT). Bimetallic CoCr-MCM-41 catalysts were synthesized by combined grafting and incorporation of metals in the framework. This synthesis allowed an increase in the maximum metal loading in the MCM-41 framework while maintaining nm-sized Co particles stable in high-temperature reactive environments. The SWNT yield was increased by more than 100% from the Co-MCM-41 catalyst. Cobalt is responsible for SWNT nucleation. The role of chromium is to anchor small cobalt particles during reduction and prevent their sintering into large unreactive particles. A larger fraction of the cobalt in the bimetallic catalysts becomes available for the SWNT synthesis when compared to the monometallic one, leading to a significant yield increase. Another effect of the addition of Cr was a shift of the SWNT diameter distribution to smaller nanotubes.
- Research Organization:
- Brookhaven National Laboratory (BNL) National Synchrotron Light Source
- Sponsoring Organization:
- DOE - OFFICE OF SCIENCE
- DOE Contract Number:
- AC02-98CH10886
- OSTI ID:
- 1020142
- Report Number(s):
- BNL--95626-2011-JA
- Journal Information:
- Journal of Catalysis, Journal Name: Journal of Catalysis Journal Issue: 2 Vol. 271; ISSN 0021-9517; ISSN JCTLA5
- Country of Publication:
- United States
- Language:
- English
Similar Records
Effect of Reaction Temperature in the Selective Synthesis of Single Wall Carbon Nanotubes (SWNT) on a Bimetallic CoCr-MCM-41 Catalyst
Effect of Manganese Addition to the Co-MCM-41 Catalyst in the Selective Synthesis of Single Wall Carbon Nanotubes