Effects of Block Length and Solution-Casting Conditions on the Final Morphology and Properties of Disulfonated Poly(arylene ether sulfone) Multiblock Copolymer Films for Proton Exchange Membranes
The effects of block length and solution-casting conditions on the final microstructures and properties of disulfonated poly(arylene ether sulfone) multiblock copolymer (BPSH100-BPS0) films for proton exchange membranes were investigated based on the basic principles of microstructure formation of block copolymers. Morphological studies using transmission electron microscopy and small angle X-ray scattering demonstrated that as the block length increased, the inter-ionic-domain distance increased, with a subsequent increase in lamellar ordering and long-range continuity. Further enhancement in morphological order was achieved by simply utilizing a selective solvent, dimethylacetamide, which is good and marginal for the sulfonated and unsulfonated blocks, respectively, rather than a neutral solvent, N-metyl-2-pyrrolidone. These morphological enhancements led to higher proton conductivity and water uptake. Drying temperature and/or solvent removal rate were observed to have considerable effects on water uptake and swelling behavior, being coupled with solvent selectivity. Also, the multiblock copolymer consisting of longer blocks was found to be more sensitive to the variation of the processing conditions such as solvent type and film drying temperature.
- Research Organization:
- Brookhaven National Lab. (BNL), Upton, NY (United States). National Synchrotron Light Source
- Sponsoring Organization:
- DOE - OFFICE OF SCIENCE
- DOE Contract Number:
- DE-AC02-98CH10886
- OSTI ID:
- 1019916
- Report Number(s):
- BNL-95762-2011-JA; POLMAG; TRN: US1103693
- Journal Information:
- Polymer, Vol. 50, Issue 25; ISSN 0032-3861
- Country of Publication:
- United States
- Language:
- English
Similar Records
High Temperature, Low Relative Humidity, Polymer-type Membranes Based on Disulfonated Poly(arylene ether) Block and Random Copolymers Optionally Incorporating Protonic Conducting Layered Water insoluble Zirconium Fillers
Disulfonated Poly(arylene ether sulfone) Random Copolymers Containing Hierarchical Iptycene Units for Proton Exchange Membranes