Processing and mechanical properties of laminar Al{sub 2}O{sub 3}-Ni{sub 3}Al composites
Conference
·
OSTI ID:10184679
Several compositions of the intermetallic alloy Ni{sub 3}Al were examined with respect to (a) their wetting of Al{sub 2}O{sub 3} and (b) their energy absorption capability in Al{sub 2}O{sub 3}/Ni{sub 3}Al laminates. Wetting is enhanced by small additions of carbon (e.g., 0.1 at. %), and bonding by additions of zirconium (e.g., 1 at. %). Chevron-notched laminate specimens were tested in three-point bending to assess the energy absorption due to the presence of a thin layer of Ni{sub 3}Al. A nickel aluminide with the composition of Ni-22Al-1Zr-0.1C-0.1B was found to have a reasonable combination of wetting, adhesion and energy absorption. Interfacial bonding was found to be weak in all laminates.
- Research Organization:
- Oak Ridge National Lab., TN (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC05-84OR21400
- OSTI ID:
- 10184679
- Report Number(s):
- CONF-940411-53; ON: DE94019332; TRN: 94:008828
- Resource Relation:
- Conference: Spring meeting of the Materials Research Society (MRS),San Francisco, CA (United States),4-8 Apr 1994; Other Information: PBD: [1994]
- Country of Publication:
- United States
- Language:
- English
Similar Records
An investigation into the fabrication and properties of Ni{sub 3}Al thin coatings on nickel substrates
The Effect of Platinum on the Growth and Adhesion of alpha-Al{sub 2}O{sub 3} Scales
Fabrication and tensile properties of continuous-fiber reinforced Ni sub 3 Al--Al sub 2 O sub 3 composites
Journal Article
·
Fri Nov 13 00:00:00 EST 1998
· Scripta Materialia
·
OSTI ID:10184679
The Effect of Platinum on the Growth and Adhesion of alpha-Al{sub 2}O{sub 3} Scales
Conference
·
Mon Dec 01 00:00:00 EST 1997
·
OSTI ID:10184679
+1 more
Fabrication and tensile properties of continuous-fiber reinforced Ni sub 3 Al--Al sub 2 O sub 3 composites
Journal Article
·
Thu Aug 01 00:00:00 EDT 1991
· Journal of Materials Research; (United States)
·
OSTI ID:10184679
+3 more