Nonstoichiometry of Al-Zr intermetallic phases
Conference
·
OSTI ID:10174408
Nonstoichiometry of metastable cubic {beta}{prime} and equilibrium tetragonal {beta} Al-Zr intermetallic phases of the nominal composition Al{sub 3}Zr in Al-rich alloys has been extensively studied. It is proposed that the ``dark contrast`` of {beta}{prime} core in {beta}{prime}/{sigma}{prime} complex precipitates, in Al-Li-Zr based alloys, is caused by incorporation of Al and Li atoms into the {beta}{prime} phase on Zr sublattice sites, forming nonstoichiometric Al-Zr intermetallic phases, rather than by Li partitioning only. {beta}{prime} particles contain very small amounts of Zr, approximately 5 at.%, much less than the stoichiometric 25 at.% in the Al{sub 3}Zr metastable phase. These particles are, according to simulation of high resolution images, of the Al{sub 3}(Al{sub 0.4}Li{sub 0.4}Zr{sub 0.2}) type. Nonstoichiometric particles of average composition Al{sub 4}Zr and Al{sub 6}Zr are observed also in the binary Al-Zr alloy, even after annealing for several hours at 600{degree}C.
- Research Organization:
- Lawrence Berkeley Lab., CA (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC03-76SF00098
- OSTI ID:
- 10174408
- Report Number(s):
- LBL--35725; CONF-9409179--2; ON: DE94016877
- Country of Publication:
- United States
- Language:
- English
Similar Records
Oxidation of Ni-rich Ni-Al intermetallics
Metastable phases in the Al sub 3 X (X = Ti, Zr, and Hf) intermetallic system
Precipitation structures and mechanical properties of Al-Li-Zr alloy containing V
Conference
·
Thu Sep 01 00:00:00 EDT 1988
·
OSTI ID:5566269
Metastable phases in the Al sub 3 X (X = Ti, Zr, and Hf) intermetallic system
Journal Article
·
Thu Oct 31 23:00:00 EST 1991
· Scripta Metallurgica; (United States)
·
OSTI ID:5879598
Precipitation structures and mechanical properties of Al-Li-Zr alloy containing V
Journal Article
·
Fri Jun 18 00:00:00 EDT 1999
· Scripta Materialia
·
OSTI ID:6176450