Environmentally assisted cracking in Light Water Reactors: Semiannual report, April 1993--September 1993. Volume 17
- Argonne National Lab., IL (United States)
This report summarizes work performed by Argonne National Laboratory on fatigue and environmentally assisted cracking (EAC) in light water reactors (LWRS) during the six months from April 1993 to September 1993. EAC and fatigue of piping, pressure vessels, and core components in LWRs are important concerns as extended reactor lifetimes are envisaged. Topics that have been investigated include (a) fatigue of low-alloy steel used in piping, steam generators, and reactor pressure vessels; (b) EAC of cast stainless steels (SSs); and (c) radiation-induced segregation and irradiation-assisted stress corrosion cracking of Type 304 SS after accumulation of relatively high fluence. Fatigue tests were conducted on medium-sulfur-content A106-Gr B piping and A533-Gr B pressure vessel steels in simulated PWR water and in air. Additional crack growth data were obtained on fracture-mechanics specimens of cast austenitic SSs in the as-received and thermally aged conditions in simulated boiling-water reactor (BWR) water at 289{degree}C. The data were compared with predictions based on crack growth correlations for wrought austenitic SS in oxygenated water developed at ANL and rates in air from Section 11 of the ASME Code. Microchemical and microstructural changes in high- and commercial-purity Type 304 SS specimens from control-blade absorber tubes and a control-blade sheath from operating BWRs were studied by Auger electron spectroscopy and scanning electron microscopy.
- Research Organization:
- Nuclear Regulatory Commission, Washington, DC (United States). Div. of Engineering; Argonne National Lab., IL (United States)
- Sponsoring Organization:
- Nuclear Regulatory Commission, Washington, DC (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 10163982
- Report Number(s):
- NUREG/CR--4667-Vol.17; ANL--94/16-Vol.17; ON: TI94014862
- Country of Publication:
- United States
- Language:
- English
Similar Records
Environmentally assisted cracking in light water reactors. Semiannual report April--September 1992
Environmentally assisted cracking in light water reactors
Related Subjects
210100
210200
36 MATERIALS SCIENCE
360103
360105
BWR TYPE REACTORS
CORROSION AND EROSION
CRACK PROPAGATION
CRACKS
FATIGUE
MECHANICAL PROPERTIES
POWER REACTORS
NONBREEDING
LIGHT-WATER MODERATED
BOILING WATER COOLED
POWER REACTORS
NONBREEDING
LIGHT-WATER MODERATED
NONBOILING WATER COOLED
PROGRESS REPORT
PWR TYPE REACTORS
RADIATION EFFECTS
REACTOR COMPONENTS
REACTOR MATERIALS
STAINLESS STEELS
STRESS CORROSION