Properties of hot isostatically pressed Bi{sub 2}Sr{sub 1.7}CaCu{sub 2}O{sub x}
Conference
·
OSTI ID:10159023
- Marquette Univ., Milwaukee, WI (United States)
- Argonne National Lab., IL (United States)
Dense Bi{sub 2}Sr{sub 1.7}CaCu{sub 2}O{sub x} (2212) superconductor pellets were made by hot isostatic pressing in an inert atmosphere. The pellets exhibited a small amount of preferred orientation of the grains. The transport critical current density (J{sub c}) values were very low for all specimens. Dislocations, planar faults, and intergrowths of the Bi{sub 2}Sr{sub 2}CuO{sub x} phase, which were produced during the pressing, caused the intragranular J{sub c} to increase substantially. 10 refs.
- Research Organization:
- Argonne National Lab., IL (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- W-31109-ENG-38
- OSTI ID:
- 10159023
- Report Number(s):
- ANL/CP--74842; CONF-920402--35; ON: DE92016394
- Country of Publication:
- United States
- Language:
- English
Similar Records
Properties of hot isostatically pressed Bi sub 2 Sr sub 1. 7 CaCu sub 2 O sub x
Characterization of hot isostatically pressed Bi-Sr-Ca-Cu-O as a function of consolidation variables
Characterization of hot isostatically pressed Bi-Sr-Ca-Cu-O as a function of consolidation variables
Conference
·
Tue Mar 31 23:00:00 EST 1992
·
OSTI ID:5024637
Characterization of hot isostatically pressed Bi-Sr-Ca-Cu-O as a function of consolidation variables
Conference
·
Thu Oct 31 23:00:00 EST 1991
·
OSTI ID:10117693
Characterization of hot isostatically pressed Bi-Sr-Ca-Cu-O as a function of consolidation variables
Conference
·
Thu Oct 31 23:00:00 EST 1991
·
OSTI ID:5958142