Development of high temperature superconductors for magnetic field applications
The key requirement for magnetic field applications of high temperature superconductor (HTS) materials is to have conductors with high transport critical current density available for magnet builders. After 3 or 4 years of being without any such object, conductor makers have had recent success in producing simple conductor prototypes. These have permitted the construction of simple HTS magnets having self fields exceeding 1 tesla at 4K. Thus the scientific feasibility of making powerful HTS magnets has been demonstrated. Attention to the technological aspects of making HTS conductors for magnets with strong flux pinning and reduced superconducting granularity is now sensible and attractive. However, extrinsic defects such as filament sausaging, cracking, misaligned grains and other perturbation to long range current flow must be controlled at a low level if the benefit of intrinsic improvements to the critical current density is to be maintained in the conductor form. Due to the great complexity of the HTS materials, there is sometimes confusion as to whether a given sample has an intrinsically or extrinsically limited critical current density. Systematic microstructure variation experiments and resistive transition analysis are shown to be particularly helpful in this phase of conductor development.
- Research Organization:
- Wisconsin Univ., Madison, WI (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- FG02-91ER40643
- OSTI ID:
- 10156514
- Report Number(s):
- CONF-9108140--3; ON: DE92015930; IN: SMRG 132
- Country of Publication:
- United States
- Language:
- English
Similar Records
Recent advances in practical superconductors
Recent advances in practical superconductors
Related Subjects
360201
665412
75 CONDENSED MATTER PHYSICS
SUPERCONDUCTIVITY AND SUPERFLUIDITY
BISMUTH OXIDES
CALCIUM OXIDES
COPPER OXIDES
CRITICAL CURRENT
CURRENT DENSITY
DEFECTS
FABRICATION
HIGH-TC SUPERCONDUCTORS
MAGNETIC FIELDS
MAGNETIC FLUX
PREPARATION AND FABRICATION
STRONTIUM OXIDES
SUPERCONDUCTING DEVICES