Characterization of melter slurries vitrified by microwave. Revision 1
Liquid high-level nuclear waste will be immobilized at the Savannah River Site (SRS) by vitrification in borosilicate glass in the Defense Waste Processing Facility (DWPF). In this facility, control of the oxidation/reduction (redox) equilibrium in the glass melter is critical for processing of the nuclear waste. As part of the DWPF process control strategy, the glass redox expected in the melter will be determined by measuring the ratio of ferrous to ferric ions in vitrified slurry from the slurry mix evaporator (SME). Chemical analysis of this vitrified feed will also be used for other process control constraints which are related to glass viscosity, liquidus, and waste component solubility. In addition, the canisters of borosilicate waste glass produced in the DWPF must comply with the Waste Acceptance Preliminary Specifications (WAPS) established by the DOE Office of Civilian Radioactive Waste Management. Specification 1.1.2 requires that the elemental composition of the glass be reported. The elemental analyses will be performed on vitrified melter feed taken from the melter feed tank (MFT). Conventional vitrification of SME/MFT slurries takes 4 hours at the DWPF melt temperature of 1150{degrees}C. Microwave vitrification of melter feed slurries has been shown to significantly reduce the time required to vitrify slurry samples.
- Research Organization:
- Westinghouse Savannah River Co., Aiken, SC (United States)
- Sponsoring Organization:
- USDOE, Washington, DC (United States)
- DOE Contract Number:
- AC09-89SR18035
- OSTI ID:
- 10129286
- Report Number(s):
- WSRC-TR--90-204-Rev.1; ON: DE92008806
- Country of Publication:
- United States
- Language:
- English
Similar Records
EVALUATION OF MIXING IN THE SLURRY MIX EVAPORATOR AND MELTER FEED TANK
Characterization of radioactive waste melter feed vitrified by microwave energy