Composition and density of nanoscale calcium-silicate-hydrate in cement
- NIST
Although Portland cement concrete is the world's most widely used manufactured material, basic questions persist regarding its internal structure and water content, and their effect on concrete behaviour. Here, for the first time without recourse to drying methods, we measure the composition and solid density of the principal binding reaction product of cement hydration, calcium-silicate-hydrate (C-S-H) gel, one of the most complex of all gels. We also quantify a nanoscale calcium hydroxide phase that coexists with C-S-H gel. By combining small-angle neutron and X-ray scattering data, and by exploiting the hydrogen/deuterium neutron isotope effect both in water and methanol, we determine the mean formula and mass density of the nanoscale C-S-H gel particles in hydrating cement. We show that the formula, (CaO){sub 1.7}(SiO{sub 2})(H{sub 2}O){sub 1.80}, and density, 2.604 Mg m{sup -3}, differ from previous values for C-S-H gel, associated with specific drying conditions. Whereas previous studies have classified water within C-S-H gel by how tightly it is bound, in this study we classify water by its location - with implications for defining the chemically active (C-S-H) surface area within cement, and for predicting concrete properties.
- Research Organization:
- Advanced Photon Source (APS), Argonne National Laboratory (ANL), Argonne, IL (US)
- Sponsoring Organization:
- USDOE
- OSTI ID:
- 1007567
- Journal Information:
- Nature Materials, Journal Name: Nature Materials Journal Issue: (4) ; 04, 2007 Vol. 6; ISSN 1476-1122
- Publisher:
- Nature Publishing Group
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Intrinsic differences in atomic ordering of calcium (alumino)silicate hydrates in conventional and alkali-activated cements
Density and water content of nanoscale solid C-S-H formed in alkali-activated slag (AAS) paste and implications for chemical shrinkage
Synthesis and nano-mechanical characterization of calcium-silicate-hydrate (C-S-H) made with 1.5 CaO/SiO{sub 2} mixture
Journal Article
·
Wed Jan 14 23:00:00 EST 2015
· Cement and Concrete Research
·
OSTI ID:22395937
Density and water content of nanoscale solid C-S-H formed in alkali-activated slag (AAS) paste and implications for chemical shrinkage
Journal Article
·
Tue Feb 14 23:00:00 EST 2012
· Cement and Concrete Research
·
OSTI ID:21596957
Synthesis and nano-mechanical characterization of calcium-silicate-hydrate (C-S-H) made with 1.5 CaO/SiO{sub 2} mixture
Journal Article
·
Sat Sep 15 00:00:00 EDT 2012
· Cement and Concrete Research
·
OSTI ID:22149361