Development of Sn-based, low melting temperature Pb-free solder alloys.
Low temperature, Sn-based Pb-free solders were developed by making alloy additions to the starting material, 96.5Sn-3.5Ag (mass%). The melting behavior was determined using Differential Scanning Calorimetry (DSC). The solder microstructure was evaluated by optical microscopy and electron probe microanalysis (EPMA). Shear strength measurements, hardness tests, intermetallic compound (IMC) layer growth measurements, and solderability tests were performed on selected alloys. Three promising ternary alloy compositions and respective solidus temperatures were: 91.84Sn-3.33Ag-4.83Bi, 212 C; 87.5Sn-7.5Au-5.0Bi, 200 C; and 86.4Sn-5.1 Ag-8.5Au, 205 C. A quaternary alloy had the composition 86.8Sn-3.2Ag-5.0Bi-5.0Au and solidus temperature of 194 C The shear strength of this quaternary alloy was nearly twice that of the eutectic Sn-Pb solder. The 66Sn-5.0Ag-10Bi-5.0Au-101n-4.0Cu alloy had a solidus temperature of 178 C and good solderability on Cu. The lowest solidus temperature of 159 C was realized with the alloy 62Sn-5.0Ag-10Bi-4.0Au-101n-4.0Cu-5.0Ga. The contributing factor towards the melting point depression was the composition of the solid solution, Sn-based matrix phase of each solder.
- Research Organization:
- Sandia National Laboratories
- Sponsoring Organization:
- USDOE
- DOE Contract Number:
- AC04-94AL85000
- OSTI ID:
- 1005411
- Report Number(s):
- SAND2003-3647J
- Journal Information:
- Proposed for publication in Materials Transactions (Japan Institute of Metals)., Journal Name: Proposed for publication in Materials Transactions (Japan Institute of Metals). Journal Issue: 3 Vol. 45; ISSN 0916-1821
- Country of Publication:
- United States
- Language:
- English
Similar Records
Properties of ternary Sn-Ag-Bi solder alloys. Part 1: Thermal properties and microstructural analysis
Hybrid microcircuit board assembly with lead-free solders