Correlation between cation disorder and flux pinning in the YBa{sub 2}Cu{sub 3}O{sub 7} coated conductor.
A correlation has been observed between the through-thickness cation disorder level in YBa{sub 2}Cu{sub 3}O{sub 7} (YBCO) coated conductor films and the commonly observed falloff in layer-by-layer through-thickness critical current density (J{sub c}) of YBCO films produced by pulsed laser deposition (PLD) on single crystal substrates. The amount of cation disorder with respect to the aggregate, c-axis-textured YBCO content was measured by Raman spectroscopy methods combined with step milling of 1.5-1.7 {micro}m thick YBCO films. For PLD YBCO films on single crystal strontium titanate, the Raman results indicate a sharp drop off in cation disorder from the substrate surface outward toward the top of the YBCO film. This drop off appears to level out in the 0.4-0.6 {micro}m range, after which the cation disorder level remains relatively constant. This trend appears to be very much like the one reported by others for the through-thickness J{sub c} dependence of PLD YBCO on single crystal specimens. Conversely, metal-organic-deposition-produced YBCO films on rolling assisted biaxially textured substrates do not exhibit a strong through-thickness J{sub c} dependence or a measurable change in the relative amount of cation disorder, again through thickness. The results of this study suggest that cation disorder in the YBCO lattice leads to increased flux pinning strength and that the cation disorder domains most probably occur on a size scale in the range from one to perhaps a few YBCO unit cell dimensions.
- Research Organization:
- Argonne National Laboratory (ANL)
- Sponsoring Organization:
- OE
- DOE Contract Number:
- AC02-06CH11357
- OSTI ID:
- 1000187
- Report Number(s):
- AND/CMT/JA-59816
- Journal Information:
- J. Appl. Phys., Journal Name: J. Appl. Phys. Journal Issue: Dec. 1, 2007 Vol. 102; ISSN 0021-8979
- Country of Publication:
- United States
- Language:
- ENGLISH
Similar Records
Structural and electrical properties of biaxially textured YBa{sub 2}Cu{sub 3}O{sub 7-x} thin films on buffered Ni-based alloy substrates.
Grain Orientations and Grain Boundary Networks of YBa2Cu3O7-δ Films Deposited by Metalorganic and Pulsed Laser Deposition on Biaxially Textured Ni-W Substrates
Inclined substrate deposition of magnesium oxide for YBCO-coated conductors.
Conference
·
Wed Dec 06 23:00:00 EST 2000
·
OSTI ID:772102
Grain Orientations and Grain Boundary Networks of YBa2Cu3O7-δ Films Deposited by Metalorganic and Pulsed Laser Deposition on Biaxially Textured Ni-W Substrates
Journal Article
·
Sat Dec 31 23:00:00 EST 2005
· Journal of Materials Research
·
OSTI ID:978174
Inclined substrate deposition of magnesium oxide for YBCO-coated conductors.
Conference
·
Fri Apr 26 00:00:00 EDT 2002
·
OSTI ID:795040